PA12G - Polyamide 12, 30% Glass Filled
LEGEND
A = amorphous - Cr = crystalline - C = clear - E = excellent - G = good - P = poor - O = opaque - T = translucent-
R = Rockwell - S = Shore
STRUCTURE: Cr
SPECIFIC DENSITY: 1.23
WATER ABSORBTION RATE (%): 0.3
ELONGATION (%): 5
TENSILE STRENGTH (psi): 13500
COMPRESSION STRENGTH (psi): 16000
FLEXURAL STRENGTH (psi): 4400
FLEXURAL MODULUS (psi): 360000
IMPACT (IZOD ft. lbs/in): 4.4
HARDNESS: R110
FABRICATION
- BONDING: G
- ULTRASONIC WELDING: G
- MACHINING: P
DEFLECTION TEMPERATURE (deg. F)
- @ 66 psi: 230
- @ 264 psi: 300
UTILZATION TEMPERATURE (deg. F)
- min: -110
- max: 230
MELTING POINT (deg. F): 350
COEFFICIENT OF EXPANSION: 0.000016
ARC RESISTANCE: 120
DIELECTRIC STRENGTH (kV/mm): 17
TRANSPARENCY: O
UV RESISTANCE: G
CHEMICAL RESISTANCE
- ACIDS: P
- ALKALIS: P
- SOLVENTS: G
More on Polyamide
BACK
|